| | | Rátáil | Córas aonad | Modh tástála |
| Maoin fhisiciúil | Dlús (23°C) | 1.2 | g/cm³ | ISO 1183 |
| Dlús dealraitheach 1 | 0.66 | g/cm³ | ISO 60 |
| Ráta leá (ráta sreafa leáite) (300°C/ 1.2kg) | 10 | g/10 nóim | ISO 1133 |
| Ráta sreabhadh toirte leá (MVR) (300°C/ 1.2kg) | 9 | cm³/10nim | ISO 1133 |
| Ráta crapadh | | | |
| Treo sreabhadh ingearach | 0.60-0.80 | % | ISO 2577 |
| Treo an tsreafa | 0.60-0.80 | % | ISO 2577 |
| Treo sreabhadh ingearach: 2.00mm 2 | 0.7 | % | ISO 294-4 |
| Treo sreafa: 2.00mm 3 | 0.65 | % | ISO 294-4 |
| Ráta ionsú uisce | | | ISO 62 |
| Sáithithe, 23°C | 0.3 | % | ISO 62 |
| Cothromaíocht, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Cruas | Cruas brú liathróid | 115 | MPa | ISO 2039-1 |
| Maoin mheicniúil | Modal teanntachta (23°C) | 2400 | MPa | ISO 527-2/1 |
| Strus teanntachta | | | ISO 527-2/50 |
| Toradh, 23°C | 66 | MPa | ISO 527-2/50 |
| Briseadh, 23°C | 70 | MPa | ISO 527-2/50 |
| Brú teanntachta | | | ISO 527-2/50 |
| Toradh, 23°C | 6.2 | % | ISO 527-2/50 |
| 23°C Briseadh, 23°C | 130 | % | ISO 527-2/50 |
| Brú briste teanntachta ainmniúil (23°C) | >50 | % | ISO 527-2/50 |
| Modal creep teanntachta | | | ISO 899-1 |
| 1 uair | 2200 | MPa | ISO 899-1 |
| 1000 uair an chloig | 1900 | MPa | ISO 899-1 |
| Modal lúbthachta 4(23°C) | 2400 | MPa | ISO 178 |
| Strus lúbthachta 5 | | | ISO 178 |
| brú 3.5% ag 23°C | 73 | MPa | ISO 178 |
| 23°C | 97 | MPa | ISO 178 |
| Brú Solúbtha agus Neart Solúbtha (23°C) 6 | 7.1 | % | ISO 178 |
| Inadhainteacht | Feidhmiú Lasair ó Dhóir Beag - Modh K agus F (2.00 mm) | K1, F1 | | DIn 53438-1, -3 |
| Ráta Dó - US-FMVSS (> 1.00 mm) | Ritheadh | | ISO 3795 |
| Teocht Adhaint Flash | 480 | °C | ASTM D1929 |
| Tástáil Glow Wire | | | EDF HN60 E.02 |
| 1.50 mm | 750 | °C | EDF HN60 E.02 |
| 3.00 mm | 750 | °C | EDF HN60 E.02 |
| Tástáil Lasair Snáthaide | | | IEC 60695-11-5 |
| Modh F : 1.50 mm | 1 | nóim | IEC 60695-11-5 |
| Modh F : 2.00 mm | 1 | nóim | IEC 60695-11-5 |
| Modh F : 3.00 mm | 2 | nóim | IEC 60695-11-5 |
| Modh K : 1.50 mm | 0.1 | nóim | IEC 60695-11-5 |
| Modh K : 2.00 mm | 0.1 | nóim | IEC 60695-11-5 |
| Modh K : 3.00 mm | 0.2 | nóim | IEC 60695-11-5 |
| Teocht Féin Adhaint | 550 | °C | ASTM D1929 |
| Eolas forlíontach | Creimeadh leictrealaíoch (23°C) | A1 | | IEC 60426 |
| ISO Gearrainm | ISO 7391-PC, MR,(,,)-09-9 | | |
| Tionchar maoine | Neart tionchair iomráiteach an bhíoma 7 tacaithe go simplí | | | ISO 7391 |
| -30°C, briste iomlán | 16 | kJ/m² | ISO 7391 |
| 23°C, bristeadh áitiúil | 75 | kJ/m² | ISO 7391 |
| Gan neart tionchair notched de bíomaí tacaithe simplí | | | ISO 179/1eU |
| -60°C | Gan briseadh | | ISO 179/1eU |
| -30°C | Gan briseadh | | ISO 179/1eU |
| 23°C | Gan briseadh | | ISO 179/1eU |
| Neart tionchair notched an bhíoma ar crochadh 8 | | | ISO 7391 |
| -30°C, briste iomlán | 15 | kJ/m² | ISO 7391 |
| 23°C, bristeadh áitiúil | 70 | kJ/m² | ISO 7391 |
| Fuinneamh tionchair ionstraimíochta il-aiseach | | | ISO 6603-2 |
| -30°C | 65 | J | ISO 6603-2 |
| 23°C | 60 | J | ISO 6603-2 |
| Fórsa tionchair buaic ionstraimíochta il-aiseach | | | ISO 6603-2 |
| -30°C | 6300 | N | ISO 6603-2 |
| 23°C | 5400 | N | ISO 6603-2 |
| Feidhmíocht theirmeach | Teocht dífhoirmithe teirmeach | | | |
| 0.45MPa, gan a bheith annáil | 137 | °C | ISO 75-2/B |
| 1.8 MPa, gan a bheith annála | 125 | °C | ISO 75-2/A |
| Teocht comhshó gloine 9 | 145 | °C | ISO 11357-2 |
| Vica teocht softening | | | |
| -- | 144 | °C | ISO 306/B50 |
| -- | 146 | °C | ISO 306/B120 |
| Tástáil Brú Liathróid (136°C) | Pas | | IEC 60695-10-2 |
| Comhéifeacht líneach leathnú teirmeach | | | ISO 11359-2 |
| Sreabhadh: 23 go 55°C | 6.50E-05 | cm/cm/°C | ISO 11359-2 |
| Trasna: 23 go 55°C | 6.50E-05 | cm/cm/°C | ISO 11359-2 |
| Seoltacht theirmeach 10(23°C) | 0.2 | W/m/K | ISO 8302 |
| RTI Leictreach (1.50 mm) | 125 | °C | UL 746 |
| IMP RTI (1.50 mm) | 115 | °C | UL 746 |
| RTI (1.50 mm) | 125 | °C | UL 746 |
| Feidhmíocht leictreach | Friotaíocht dromchla | 1. 00E 16 | óm | IEC 60093 |
| Friotaíocht toirte (23°C) | 1. 00E 16 | óm·cm | IEC 60093 |
| Neart tréleictreach (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| toilleas coibhneasta | | | IEC 60250 |
| 23°C, 100 Hz | 3.1 | | IEC 60250 |
| 23°C, 1 MHz | 3 | | IEC 60250 |
| Fachtóir diomailt | | | IEC 60250 |
| 23°C, 100 Hz | 5. 00E-04 | | IEC 60250 |
| 23°C, 1 MHz | 9.00E-03 | | IEC 60250 |
| Innéacs rian sceite | | | IEC 60112 |
| Réiteach A | 250 | V | IEC 60112 |
| Réiteach B | 125 | V | IEC 60112 |
| Inadhainteacht | Rátáil retardant lasair UL | | | OL 94 |
| 2.50 mm | HB | | OL 94 |
| 0.750 mm | V-2 | | OL 94 |
| Innéacs inadhainteacht na sreinge te | | | IEC 60695-2-12 |
| 0.750 mm | 850 | °C | IEC 60695-2-12 |
| 1.50 mm | 850 | °C | IEC 60695-2-12 |
| 3.00 mm | 930 | °C | IEC 60695-2-12 |
| Teocht adhainte filiméid te | | | IEC 60695-2-13 |
| 0.750 mm | 875 | °C | IEC 60695-2-13 |
| 1.00 mm | 875 | °C | IEC 60695-2-13 |
| 1.50 mm | 875 | °C | IEC 60695-2-13 |
| 3.00 mm | 900 | °C | IEC 60695-2-13 |
| 11 Innéacs ocsaigine a theorannú 11 | 28 | % | ISO 4589-2 |
| Maoin optúil | Innéacs athraonach 12 | 1.586 | | ISO 489 |
| Tarchur | | | ISO 13468-2 |
| 1000 µm | 89 | % | ISO 13468-2 |
| 2000 µm | 89 | % | ISO 13468-2 |
| 3000 µm | 88 | % | ISO 13468-2 |
| 4000 µm | 87 | % | ISO 13468-2 |
| Céim ceo (3000 µm) | < 0.80 | % | ISO 14782 |